  1. wegm

    Pipeline Welding Techniques

    thandion, It's true that GTAW gives good root but if you prefer higher productivity you can switch to GMAW-STT that is a type of GMAW process with which root can be effectively welded. Please have a look at this link: GMAW-STT (Surface Tension Transfer) for CS regards, wegm
  2. wegm

    filler metal for dissimilar material welding

    Mohamedhassanmido, Please have a look at this link that suggests filler metals for similar and dissimilar materials welding: Filler metal, preheat and PWHT selection guide. Moreover for some specific cases of dissimilar material welding you could have a look at these links: Monel 400 (UNS...
  3. wegm

    Pipeline Welding Techniques

    thandion, It's true that GTAW gives good root but if you prefer higher productivity you can switch to GMAW-STT that is a type of GMAW process with which root can be effectively welded. Please have a look at this link: GMAW-STT (Surface Tension Transfer) for CS regards, wegm
  4. wegm

    NDE requirements for valve by-passes

    MSOHRABI, API 6D doesn't require obligatory NDTs. Instead, if your client requires NDTs then you shall perform them as specified in Annex A of API 6D. For example if MT on welds is specified by the customer, you shall perform it as specified in clause A.13 of Annex A. Please have a look at this...
  5. wegm

    Is 316SS commercial requirement require UT test ?

    katrinali, Regarding your original query, please let me add that the requirement for UT depends on the applicable code and customer requirements regards, wegm
  6. wegm

    Is 316SS commercial requirement require UT test ?

    denlow60, Please note that "non-magnetic" isn't a restriction to perform UT as it is for MT since UT doesn't require the magnetic properties of a steel. katrinali, UT is widely used for austenitic stainless steels like SS 316 even though the austenitic structure makes it difficult to detect...
  7. wegm

    Welding Dissimilar Metals

    zmazim, I agree with metengr's recommended practice though I would like to highlight that the 316 filler metal shall be used to finish up the welding if the welding overlay of CS pipe has been externally performed. Otherwise, if it has been internally performed, you shall finsih up the welding...
  8. wegm

    Welding dissimilar materials

    Metengr, Since andysf wrote "25/12 casting", I suppose it is in accordance with ASTM A 447 (standard specification for steel castings, Chromium-Nickel-Iron Alloy, 25-12 Class, for high-temperature service) and even though the chemical composition of E309 is closer to that steel than the...
  9. wegm

    API X52N VS X65

    Gkvengat, As per API 1104 a change in base material constitutes an essential variable and for that reason all materials are grouped as follows: a. SMYS (specified minimum yield strength) =< 42 Kpsi b. 42 Kpsi < SMYS < 65 Kpsi c. for materials with SMYS >= 65 Kpsi, each grade shall receive a...
  10. wegm

    Welding dissimilar materials

    Andysf, I agree with metengr that E309 welding consumable is a good choice for such a welding though I would like to highlight that it is recommended only for standard temperature service (SFA-5.4, A7.10, E309 states: "Embrittlement or cracking can occur if these dissimilar steel welds are...
  11. wegm

    Another Hydrogen Bakeout Questions ASME Sect 1 work

    rmillercwi, As stated in AWS D10.10 hydrogen bake out is performed to remove hydrogen from material prior to manufacture, fabrication or repair activity. So the process is used not only after welding or repair welding but also in some cases before welding when the base metal contains hydrogen...
  12. wegm

    Welding 316L to A36

    Steris, With regard to your question for annealing/stress relieving, please have a look at SFA-5.4, A7.12, E309L that states: "Embrittlement or cracking can occur if these dissimilar steel welds are subjected to a post weld heat treatment or to service above 700 degree F". So, as Metengr told...
  13. wegm

    Pipeline Topside Riser API1104 API5LX52 16inch with Weldolet 6&quot; branch

    ThanaQC, Please let me add that the existing qualification doesn't qualify for your production welding since the essential variable 6.2.2 (d) doesn't apply (the qualification has been done on 16" circumferential weld and you are to weld 6" circumferential weld and thus you shall change outside...
  14. wegm

    Pipeline Topside Riser API1104 API5LX52 16inch with Weldolet 6&quot; branch

    Steve, I don't agree with you since the API 1104 doesn't specify that branch welder qualification test shall be done only if it is a project requirement. ThanaQC, Since it is for full penetration welding you shall follow the 6.5.1, Figure 12 for single qualification or you shall perform multiple...
  15. wegm

    PQR qualification confusion

    gkvengat, Even you have not told us the applicable code, the 10.3 mm could qualify for such a variety of thicknesses to the majority of codes regards wegm
  16. wegm

    PQR qualification

    Jusplayn31, Regarding the whole welding, there is no reason to perform grinding neither on the root nor on the cap since the dimensions on the sketch of the "sample procedure specification form" are for example only as clarified by the form's note. Regarding the excess reinforcements of the test...
  17. wegm

    API 1104 Procedure Qualification.

    alkeeprollin, You can not use procedure that qualified with X70 in order to weld X65 to X42 because it is not permitted by par. 5.4.2.2 c of API 1104 (for materials with a specified minimum yield strength greater than or equal to 65.000 psi, each grade shall receive a separate qualification...
  18. wegm

    welder qualification

    Tman1, According to AWS D1.1, table 4.12, variable 2, a re-qualification of welder is required when the SMAW electrode has F-number higher than the WPQR (welder performance qualification record) electrode F-number. So, in this regard your welder could use SMAW electrode with F-number 1 or 2 or 3...
  19. wegm

    9cr Bakeout

    rmillercwi, The post-weld hydrogen bake out in such a case depends basically on the base metal thickness and since you are to weld 4" weldolets to a 16" pipe, I suppose that the base metal thickness is much more higher than 15 mm and thus post-weld hydrogen bake out is recommended. In addition I...
  20. wegm

    Welding between duplex and inconel/SS316L

    Sorry, the above link doesn't work, you could have a look at this link: http://www.weldinguide.com/gdanastasiadis/viewtopic.php?f=2&t=9