I'm working in a perforation plant. We have some difficulties with the small dia (1.5 mm) punches. Material to be perforated is soft galvanised steel in 0.5 mm thickness.
I guess the material (HSS) and/or heat treatment (60 HRC) is not good enough for the punches.
Can you advise your experiences regarding this subject?
Thanks in advance.