Condensate corrosion due to CO2 is usually handled by neutralizing amines added to your BFW, they can be formulated in various ways depending which condensate system (HP, LP, etc) you are having problems with.
For your condensate piping, carbon steel would be a typical material to use. What have you seen from a failure analyses of the cracking?