Yes. For most pressure vessel steels, a liquid quench and temper heat treatment assures a rather consistent, through-thickness microstructure, which enhances fracture toughness properties. In comparison, a normalization heat treatment may only involve rapid cooling in air that would increase strength over annealed material, but not necessarily result in a through-thickness microstructure with improved fracture toughness properties as a quench and temper heat treatment.