Hi
Thanks for your reply's. Here is the additional information as requested:
1) Wall thickness after deep hole bore 10 - 25mm
2) Base thickness up to 45mm
3) No concerns over service temperature ranges
4) Corrosion resistance - Components are plated, specification dependant on location &...
Can anyone recommend a steel with the following properties:
1) Must be available in solid billet form up to approx 175mm to allow deep hole boring operation to take place.
2) Material must be weldable, preferrably using the MIG / MAG or TIG processes.
3) Must be heat treatable to achieve a...
I am looking for information regarding Nitrocarburising - can any one point me in the direction of a website or supply me with a little information.
Thanks
Thanks for all your replys - much appreciated. Will conduct a inclusion count and check grain size. Q&T details are hard to come by as this material was treated in China - They have been requested but so far are not forth coming.
I recently Charpy V notch tested some 50Mn2 steel (CMn steel %C 0.47 - 0.55, % Mn 1.4 - 1.8 & % Si 0.17 - 0.37), in both the quenched and tempered and forged conditions. I have a Rp0.2 of 650 - 700N/mm² & Rm value of 900N/mm² & a % elongation value of between 16 - 20%. Values were taken at...
HI ALL
CAN ANYONE TELL ME OF A STANDARD FOR EVALUATING RESULTS OF CASS TESTS.
THE COMPONENT CURRENTLY UNDER TEST IS A FeC BASE METAL, WITH A BRONZE / CHROME FINISH, WITH A PLATING DEPTH OF 75 - 100 MICRONS.
IF THERE IS NOT A STANDARD CAN ANYONE POINT ME IN THE DIRECTION OF INFORMATION?
BEST...
HI ALL
CAN ANYONE TELL ME OF A STANDARD FOR EVALUATING RESULTS OF CASS TESTS.
THE COMPONENT CURRENTLY UNDER TEST IS; FeC BASE METAL, BRONZE / CHROME PLATING, WITH A PLATING DEPTH OF 75 - 100 MICRONS.
GRADES OF 10 AFTER 1000HRS ARE ACHIEVED USING NSS TESTING, WHICH HAS LED ME USE A MORE...