Recent content by amit217

  1. amit217

    Query for requirement of HAZ impact specimen removal as per SEC VIII-Div I; UG84(g)(2)

    Thanx Mr David
  2. amit217

    Query for requirement of HAZ impact specimen removal as per SEC VIII-Div I; UG84(g)(2)

    I have one query regarding Impact specimen removal of HAZ as per SEC VIII-Div I UG84(g)(2). Case – welded PQR with single side welded only one process. Base metal thickness is 8 mm. So question is can I prepare 7.5 mm thick impact specimen which is nearest obtainable thickness from 8 mm base...
  3. amit217

    Impact Location of HAZ Specimen as per ASME SEC VIII Div I UG-84(g)

    thread292-376038 Hello Going to qualify new PQR with base metal thickness 8 mm, So as per UG-84(g)at which location I have to remove HAZ impact specimen, as I can obtain 7.5 mm thick standard sub-size impact specimen from 8mm thick plat ? as per fig. UG-84.5 and Table UG-84.6 for base metal...
  4. amit217

    Welding of AISI4140 to SA240 TP316L

    Thank you for you advice
  5. amit217

    Welding of AISI4140 to SA240 TP316L

    Hello I want to weld AISI4140 to SA240TP316L, Please advice me which electrodes I have to use