Physical properties of A2 Tool Steel after hardening to HRC 58-60 2
- Thread starter Frogwort
- Start date
-
1
- #2
-
1
- #3
EdStainless
Materials
Modulus is a physical property, and HT condition will not change it.
Yield is a mechanical property, and at this hardness there really isn't much of a yield.
I would be surprised if you can get any measurable elongation at failure, it will be very brittle.
= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, Plymouth Tube
Yield is a mechanical property, and at this hardness there really isn't much of a yield.
I would be surprised if you can get any measurable elongation at failure, it will be very brittle.
= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, Plymouth Tube