You are telling me what I want to hear. But I haven't found anything in writing yet that indicates it will prevent the yield point elongation.

Thank you, I know it is not a surprise. High strength steel won't work with the tooling that has been made. It may be possible to specify a Nb or V fine grained material, but some info I have indicates that it will also dissolve at 2000F. Also, I want to get rid of the upper lower yield point...

Hello Everyone. I am new to this forum. I am working on a steel assembly that is made by brazing low carbon steel (call it 1005 for now) with a more or less pure copper braze filler at 2000 degrees F or about 1095C. The material is experiencing some erratic grain coarsening, especially in cold...