Yes i meas the Annex A.2.3.
if i read the ANNEX A that meas:
"Subject to A.1.2, A.1.3, A.1.4, and A.1.5 below, the CRAs and other alloys listed in Table A.1 to Table A.42 may be used without further testing for SSC, SCC, and GHSC cracking-resistance within the environmental limits shown."
If I...
Dear all, I have a question about welding on austenitic stainless steel according to NACE MR0175. In the PQR, do I need to demonstrate that the hardness meets the requirements?
Does the PQR need specific tests to comply with NACE, or is austenitic stainless steel implicitly compliant?
best regards,
@weldstan
I agree with you, i think that need to improve the preheat and heat imput
@r6155
The hardnees of the report on base material meet the naece requrement, more precisely, the maximum value found is 240 HV
@Sjones
Carbon Equivalent [CEQ] 0,41
Carbon Contenet 0,19
thanks to ALL
Dear All,
I need help
we performed a butt weld ( full penetration ) qualification with the following characteristics:
ASTM A350-LF2 to ASTM A333 GR.6
Thickness of pipe 5,54 [mm]
Diameter of Test Coupon 60,30 [mm]( 2 inc )
Welding Process(es) GTAW
Poition 6G
Amps. 100 to 130
Volts 15 to 16...
A well-known supplier of welded load ring, claims to supply an S355J2+N with impact test at -45. shouldn't he call it S355J4 / J5?
Can S355 reach these temperatures?
Thanks in advance for your answers
thanks for the reply, I did not specify that I am in the QW-403.6 impact test regime (The minimum base metal thickness qualified
is the thickness of the test coupon T or 5/8 in.)(16 mm),. Actually I wanted to qualify higher thicknesses, and the QW 202.4 says that with MB greater than 38mm the...
I have to weld a T-joint in full penetration with dissimilar thicknesses in Asme IX. Both materials are in carbon steel (P-N.1.2) the only QW that speaks of dissimilar thicknesses is QW-202.4.
Base material 1 thickness 8mm
Base material 2 thickness 35mm
the QW-202.4 for the CS refers to the...