I have several failed fasteners. After metallurgical evaluation the failure mode is classical grain boundary embrittlement (rock candy fracture surface, cracks along prior austenite grain boundaries in micro). Hydrogen embrittlement, right? However, these fasteners were not plated (cad, zinc...