These are my parameters.
Corrosion resistant
Actual stress through design is low, but there is a contact stress that could cause deformation. Materil Rc40 and harder solve this.
I was looking a stainless steel type material that can be heat treated to Rc 40 min.
I was looking at 440C
Is there...
I have a steel casting that is quenched and tempered and then machined
Weld repairs were performed after the machining.
I am assuming the casting should be re-heat treated.
Is it typical to just re-temper? or a full Q&T?
Is there a time frame to complete this after the welding is performed...
I am aware of some of the advantages in cold vs hot rolled products.
This is what I have:
1050 steel shaft, currently cold rolled and turned down to size, and threads added.
Possible savings in switching to a hot rolled product.
The UTS/YTS of the hot rolled product is less, but still within...
If I have a shaft that has one end set at -A- and another feature set as -B-
I then define my primary for other features to reference A-B
Can I set a control to define the position of B in reference to A?
Or would this not be acceptable since A-B is the datum for other features.
Imagine the a tie rod end.
The sphere component has a shaft protrusion.
For functionality in the assembly, the sphere is the primary datum.
If I called out the diameter of the sphere as the datum would be it be a center point? Or a set of perpendicular planes?
Just wanted an opinion on this one...
This is my thought on the subject.
Plate with a hole in the center.
The center hole is created by holding the bottom surface and 2 sides.
The plate is assembled by placing a bolt to the hole and clamping against the large bottom surface
I would do the...
Can someone explain the expected change in surface finish after a part is subjected to electroless nickel plating?
I would expect the finish to measure a bit rougher.