Good Morning Yes as the title If I manufacture a stator will that wirecut surface degrade my electrical quality Thank you

I have wire cut a 40 mm 12 tooth , 0.5 mm lamination thickness stator piece , there are 16 pieces Im doing a skip tooth Classic LRK wind large prop at about 4000 RPM Do I need to anneal the stator pieces after wire cutting Does wire cutting greatly effect the properties of the steel or...

How do you remove that dark oxide layer on SS Portions of my parts are very narrow with small holes 3mm and I cannot quite get the TIG brush in the area Also ,,, Tig brush creates heat which can warp slender parts Can you recommend some powerful pickling ???? Thank You

Its 10 Al 68 Copper and 4% iron Turned out more Magnetic than 316 So Can it be removed by electric means I dont want to heat very high as they are longish bars Thank You

Colleague, has a SS tube 30 Dia by 400 long with an oil seal type running on the 30 dia Slowly Usually wet But can turn dry Approx 10% salt water Looks like a galvanic type corrosion at the seal area No heat involved Can you recommend a metal , SS ? I dont think plastic will do...

I need a pill 2mm Dia by 1 thick with a 1 hole thru , pure I have manganese powder can it be vacuum melted in say a 3mm pyrex tube , then machined to size I hear its hard and brittle , what Rc would that be Thanks

In Astropysics equip there is a tendancy to use SS for bearing elements No rust I worry that some parts I make such as a bearing elements from 316, at dimensions 120 x 60 by 12 thick out of bright bar What is your estimate of stability over time with out heat treat

Good afternoon I am tempering 431 in the range that adversly effects corrosion resistance I suppose its the chrome thats depleted Final hardness is 42 Rc My part runs at 40,000 PSI in pure water Would pressure also deplete corrossion resistance

Good Morning I have to screwcut , some 30mm Dia bars of this Matl used as a pressure vessel , 40,000 PSI / 800C Can I get an idea of the machining characteristics Thank you

Have got a room size vacuum system with inside parts that need accurate alignment relative to one another Height wise too Is there a large laser or similar system that will resolve about 10 thou in 3D The aero people must have this down pat with their big structures Thanks

With sintering,,,, the metal is not melted as in casting Its compressed then heated to below its melt point Is this right ? Thats the question thanks

I have a Hydraulic motor that is 19 ft/lbs at 2000 PSI What would the stalling torque be? ,,,,,,, much higher or maybe not Thanks

I guess a Silicon Carbide type wheel But are there any modern specials or designations that are good? Thanks for any replies

How can I stress relieve a largish 316 forging after machining, its 500 by 400 by 900mm Thanks

Great minds What does PS mean in relation to Horsepower Thanks 123Cat

Im running 3,800 ft/min on a 38A grinding Wheel on a High Speed Steel Job this is a bit slow isnt it? Thanks 123 Cat

Does 530C then turn the oven off sound good to you ? I think thats it Thanks 123Cat

Can any of you fine men tell me where I can get info on fitting these bearings For Eg a 10 mm OD bearing , What size hole is it' a 10mm reamed hole or a reamer that cuts 1 thou under size I want to get it right so the bearing works correctly Many Thanks 123Cat

Im machining a V block from 316 SS ,,,,,450 long by 70 mm square And it has to stay dimensionally stable within 1 thou over about 20 years Im doing it out of bar stock If I just rough and machine it without any heattreatment would it be OK And also can you recommend a heattreatment to...

Im looking for the oil or additive that helps 2 stroke GP 125CC engines survive at the end of the sraight when the throttle is closed There is one 123Cat