I am trying to meet these properties below but for some reason after performing the Heat treatment listed below, I got different results. Part is 6.6" thick. I cannot give anymore than that sorry.
UTS(Ksi)
min: 95
Max 115
Yield(.2 Offset/Ksi)
min: 80
Max: none listed
Elong(2")
Min: 20...
Good Morning,
What are the best business practices for forging Ti-6-4 to aerospace quality?
Is it okay to forge Ti-6-4 in a furnace that is also used to forge Fe based pieces?
The Ti-6-4 is typically forged around 1700F-1775F while our Steel is forged usually above 2200F? I am worried that...
Does all 15-5 need to be cooled to 70F? We are wondering at my company if cooling 15-PH to 40F or below would give us better mechanical properties?
We usually get material that is with the .5-.7 range. My previous company used to require that we always held our manganese within the .75-.9...