We use strip in a continuous process & have found the welded joint on 15% cracks every time it is formed not at the weld but at the HAZ. This material would seem to be of little use unless it is used without joining?
What about the reduction in strength at the joint, the 1/4 hard will be soft at this point due to heating in our experience - is there a way to combat this?