Thanks for the responses!
Compositepro, the handle will have a specific shape to it, so the dip coat doesn't sound like it's a viable option.
btrueblood, You point out some things are becoming very apparent to me. That is there are many ways to make this work. Sometimes too many choices is...
OK, look like I can't send a message privately. Or I am just not seeing how it's done. So I will try to answer your question as best I can.
This hammer will never strike anything metallic or anything harder than the sole of a work boot. So stuff that is non-rigid. Sorry for the vagueness...
Thanks for the response!
I will look into your recommendation. In regards to the striking surface, I will send you a private message. There is a patent pending on this, but I rather err on the side of caution.
Thanks again.
Hello,
I'm designing a sledge hammer that will have a steel handle that will be over-molded in rubber. There are other products on the market that already do this, but I don't work for these other companies. So, what rubber would be suited for that application? Oh, I'm talking about the big 3...