Thanks you for your replies and sorry for the delay in replying. @metengr: The values in mechanical properties are down by atleast 15 to 20%. I dont have the exact values with me at present. @ btrueblood: The Chemical analysis of the sample showed Cu:86.9 Al:0.003 Sb: 0.21 Fe:0.15...

Thank you TVP for your reply, As you rightly said, our component is an pump Impeller which sand cast and is then machined. We did a test for mechanical properties and the tensile strenght and elongation were lower compared to the standard properties given for C92600. So we were wondering if we...

Hii, As you all know C92600 contains the following composition, but this composition isnt giveing us the desired mechanical properties. Can some tell which alloy elements would influence values of tensile strength and elongation? Cu:86.0-88.5 Al:0.005 Sb: .25 Fe:0.20 Pb:0.8-1.5...

Hi, I was conducting a structural analysis for a very critical component subjected to pressure & temp, material-ductile iron. I used a solid 92-tetra element and carried out the analysis. The stress was within acceptable limits during this analysis. But when I started to vary the temp, the...

Hi, I would to know the yield strenght for various grades of gray CI. I know people use 0.2%y , can someone indicate the values or indicate any website. This for an analysis project, using a software which requires yeid strength. thanking you san

hi, I have been trying to create the vanes of a centri pump(i want a final solid not surfaces)using proe2001. Using the curves(4 nos, 2 upper and 2 lower) i have been able to create surfaces using the boundaries option. Now i tried creating a protusion with the quilt option i.e after merging of...

hi, When I try to import a dxf file into UG 17, I get a message that says "scaling from mm to inch". My drawings are in mm and I would like UG to import it in mm. This face the same problem when i try to import it into a new or a work part. I havent tried importing dxf into 18 or NX. Please help...

Hi, I have a profile that I would like to pattern it over a cylindrical surface. I have tried to wrap the profile over the cylindrical surface and then extrude it, but it turns into a sheet.How can I create a solid body out of this method? Is it possible to pattern a general pad? Please do help...

Hi, Recently I upgraded my system from 98 to 2000 Prof using the upgrade option. Since then I am not able to run Proe2001.A black screen appears and then it disappears. please do help.Is it a problem with the installation of win2000? sansvk

Hi, Thanks for the help. Its for our company, they had procured IDEAS long back but we dont use it. We use Pro/E instead. I just wanted the information so that I could install and compare the two softwares. Which one do you think is superior for modeling. sansvk

Hi, I am not used to working in IDEAS, but I would like to install IDEAS on my computer. Please can someone tell me on which OS does it work. I have IDEAS ver 8. I have heard it doesnot work on win98 & win ME, does it work on win 2000 prof, NT. please do answer. sansvk

thanks atlarson(Mechanical). Your tip on importing really worked,although I had to spend some time over it,the results were fruitful.

hi, when I import dxf files to proe2000i, a warning arises about the format size. I use mm in autocad. How do I select units in 2000i and please tell me how to change the tolerence or accuracy limit between two points during importing.please do help me solve the problem. thanking you in advance.

Can anyone help me out with creating datum planes on the fly so that I could use them during patterning.

Hi, I am into modeling swirlers and turbines. I would like to know how to pattern components that are created using offset command.I have tried to pattern, but I was not sucessful. I think the problem lies in the surface that I choose to offset,because it is considered as a reference. Please do...