Recently we have done welding process for aluminium 6061 T6 material fillet welding base plate 12mm thick with 40mm rod with proper wps and maintenand process parameter
But it was failed during macro test due to not pentrent weld metal
Please suggest how to solve the issue
Thanks in advance...
Hi thanks to all
For your valuable inputs
Here Material is 6061 T6 condition after welding we have done tensile testing weld sample without any anealing treatment and it is failed
As per your post comments we under stand that any such type of 6061 T6 codition materials should not do the tensile...
Hi
Thanks everyone for your feed back
1) aluminium 6061 T6 codition material we have welded for qualification as per WPS as per ASME SEC IX guidelines
Here my question is after welding the above 6061 T6 materials is it required tensile testing weld sample or not?
If it is radiography report ok...
Thank you for your response and we wil do that
Secondly I have clarification on welding symbols
Please help me how to study the following welding symbol on drawing
Thanks & Regards
PVKRaju
thread725-355292
Hi
This is PVKRaju
I am also new for welding and I would like to know the welding qualification as per ASME SEC IX for aluminium 6061 material
Please suggest
Thanks in advance
Regards
PVKRaju
Hi
Thanks for immediate response
Still I am waiting more suggestions from others
If required I will share photos color shade variations
Pleae suggest
Thanks in advance
Regards
PVKRaju
Hi
This is PVK Raju
I would like to know the Zinc plated parts acceptance criteria
Recently we have received parts from our supplier after Zinc plated as per ASTM-B-633 SC2, Type2 on that we have found visual appearance, like colour shade variation
Please suggest how to justify the color shade...