Thankyou for the answer Clvet. We have dropped telflon sheet idea.
FYI: the sheet was going to be used against liquid iron short exposure. Which obviously is not possible with teflon ( now we know ).
We will opt for our conventional way of using refractory coatings ( BN or Zr, water based )...
If a TPFE applied steel sheet (less than 1mm diameter) is exposed to a temperature of >327C it will disintegrate quickly with in 2 minutes.
Is there any way that i can prolong disingration time to seven minutes? changing thickness? using some special type?
I want to use it on a consumable...
CoryPad :: Melting point > 1300 °C is your obstacle. There will be no cheap metals, so a ceramic does seem like a good choice. Any other limitations? Resistant to HCl, must hold a liquid, other?
It is exposed to liquid metal for short time. it will be used once. All it needs to do is to...
I am looking for a cheap material to replace deep drawn steel sheet in a product. Steel sheet is coated with ceramic coating and used in high temperature applicatioins. I have tried ceramic cloth ( metal reinforced and moulded in different shapes with the help of fiberglass). It works almost...