I would rather not have any pre or post weld treatment. The cast part in question is a seat post pivot that will be used on durable medical equipment. The question from our investment casting vendor is if we need to heat treat the part prior to welding it onto the seat post. The information...
What possible material conditions would result from welding non-heat treated cast 8620 that should be taken into consideration in a load bearing application?