Recent content by lesniowski

So you are telling me that the test will tell me if the part is cured properly or resin rich?

What is the purpose of doing an acetone extraction test on molded phenolic parts?

This was just an example to ask a question about units. I'm sorry if this made anyone ponder about what type gun or bullet. CoryPad answered my question. Thanks

$100K ! ! ! a scheduler makes $100K WOW!!!!!!!! It sounds like you need someone to coordinate the jobs in your shop. No planning software can help you on a fast paced job shop unless you have someone to coordinate between projects. I would suggest that you hire a planning/scheduler that would...

Yes I have seen that figure. I am still trying to find the correlation between shore D to Barcol.

If a bullet is shot out of a gun at an acceleration of 1000 g's is the acceleration 1000*32.2 ft/sec^2?

diamondjim Thanks, I already saw that URL and it doesn't provide a conversion between Rockwell M to Barcol. I have even been trying to find rockwell M to shore D and then shore D to Barcol but I haven't had much success.

Where can I find a conversion of Rockwell Hardness "M" Scale to Barcol Hardness?

I WANT TO PERFORM NONDESTRUCTIVE TESTING ON MARAGING LIKE MAG PARTICLE INSPECTION.

The temperature is 15F to 120F. The coating should be tough enough to be handled and moved by cradles and carts.

I am looking for corrosion protection for C300 and C250 maraging steel. Must pass high humidity, salt water environment.