Recent content by FinishingTalkdotcom

  1. FinishingTalkdotcom

    Zinc Plating

    There are many clear chromates on the market, some offering much more corrosion protection than others. For example, we have a clear chromate that will pass 48 hours in salt spray to red rust, and another that will pass 120 hours. We offer zinc plating with clear/blue, yellow, and black...
  2. FinishingTalkdotcom

    Zinc Plating

    There are some things the plater can do to enhance corrosion resistance. Zinc dust, hydrogen peroxide, and carbon treat the zinc solution periodically. This removes metallic and organic contamination that can contribute to premature corrosion. Also, the plater should check the bottom of the...
  3. FinishingTalkdotcom

    Dry Paint Filters - Spontaneous Combustion?

    Stacking the filters can trap fumes from evaporating, causing friction, thus heat, thus fire. We have incorporated this dry filter system as well. Our procedure is to hang the filters to allow them to completely evaporate and dry, then disposal. Hope this helps.
  4. FinishingTalkdotcom

    Suggestions and tips for a small in house plating plant.

    Feel free to check out our site as well. www.finishingtalk.com It is full of members with years of experience eager to answer questions relating to plating and finishing.
  5. FinishingTalkdotcom

    Suggestions and tips for a small in house plating plant.

    There is too much info to list on this reply. I would recommend contacting a consultant for help with this installation. You can find one at www.finishing.com. They can walk you through the environmental issues (air and waste water), technical analysis of all plating solutions, and line set-up...
  6. FinishingTalkdotcom

    Painting Valves

    What type of phosphate? Iron phosphate would be more economical, but unless the parts are painted immediately after phosphating, they could begin to flash rust. This would not promote but would decrease adhesion. If you need more storage time between phosphating and painting, may want to...
  7. FinishingTalkdotcom

    Want to be involved in the coating industry

    First, congratulations on joining our industry! The momentum of our industry always presents opportunities. I agree with the previous posts to join associations to keep updated with current issues. These issues often present opportunities, such as EPA regulations, OSHA regulations, etc. For...
  8. FinishingTalkdotcom

    Zinc and 300 series combination

    Ionic Zinc reacts with ionic chromium (in its hexavalent state) in an acidic catalyzed solution to form zinc chromate. I would not think this reaction should occur in their uncharged state as metal. The only reaction I would expect is the zinc corroding, which is why zinc is sometimes referred...
  9. FinishingTalkdotcom

    Black Anodize over 6061-T6 Al - Defect Question

    Also need to check substrate. If any alloying metals are present in this area, can affect appearance of anodize coating.
  10. FinishingTalkdotcom

    Protecting CDA 260 Brass from Dezincification while annealing

    The majority of the parts we anneal are 70% Cu / 30% Zn. We anneal at 500 degrees F for 8 hours, gas fired oven, normal atmosphere. I have completed exhaustive stress corrosion experiments with gases from ammonium chloride solutions (raised to pH of 10.0) and mercurous nitrate solutions. The...
  11. FinishingTalkdotcom

    Surface finish after nickel plating

    Electroless Nickel should mimic the surface of the substrate. If the substrate is polished, the EN plate will be bright - if the substrate is etched, matte finish (assuming all components are within their operating parameters).
See more