sodeen - I agree with you. This is about the only method that I have right now that gives me a clue this is going on. But when looking at the structure I do not see anything that leads me to believe that I am seeing retained austinite.
TVP - The link didnt seem to produce an article on this...
We use 10% ucon-b at 110f in quenchant. I have always suggested using high quench volume. What would be a satisfactory preheat temp? Is it advisable to temper freeze temper after induction. I have found some information that says to just freeze and then temper after induction and it should be...
I would like to receive some feedback on methods for induction heat treating 440c. I know this is a difficult procedure, but I also know it can be done. If anyone has any experience in this area I could use some advice. I am very interested in the process of preheating material prior to...
I would like to receive some feedback on methods for induction heat treating 440c. I know this is a difficult procedure, but I also know it can be done. If anyone has any experience in this area I could use some advice. I am very interested in the process of preheating material prior to...