    Overaging IN718

    thank you very much for this, Is there a way to calculate the maximum hardness you can achieve by the composition? Thanks again for this, I will look into what you have said. It looks like we use the NACE oilfilled HT then kind regards Augustus
  2. Augustus1

    Overaging IN718

    Good Afternoon, I am after some information about IN718. I have reviewed a number of documents and the maximum HRC is around 40-42, I am wondering why you couldn't increase that to 46HRC value. I am looking at a HT cycle of solution treat, 1010C 2hrs, then a double age 750C 8hrs furnace cool...