Recent content by Aubryann

never mind, I got it! Thanks

It is called out on a military print but I have never heard of it before and when I do a web search it didn't bring up what I'm looking for. Any help would be much appreciated...thanks

thanks again... I think I'm going to go with a thin plastic coating from 3M.

thanks Cory...that's what I was researching but I think the coating would be almost as thick as the material, .010.

my bad...60 C, not 600

hello everyone. I did a search but did not find anything related to what I'm looking for help on. I need a help finding a non-stick coating for 99.99% Indium foil that will meet these specifications. Non stick barrier on one side of material must not stick to copper, aluminum, or nickel plated...

hello everyone. I have surgical parts that are 17-7 SS (.050 thick)annealed that were heat treated per RH 950 to RC 45 min, but they were not heat treated in a vacuum atmosphere as directed so they are discolored. Our in-house cleaning methods will not work. Is a bright dip a good...

Hi everyone. I have done several searches on this website with no luck. Does anyone know or can lead me to the specification for biological approval: Q1153A-ISO 2 ER for 17-4 stainless steel? Any help would be appreciated. "If this post shows up more than once I apologize. I was having trouble...

thank you very much everyone for all your help. Have a nice holiday! Aubry

hello everyone. I hope you all had a nice Thanksgiving! Back to my inquiry. Do you all agree that with the material's composition that has the higher Mn shouldn't have an affect on the Nickel plating? The reason I'm bringing this up is because my plating vendor insists it has something to do...

The reading I received was 07 C 43 Mn 016 P 008 S Not sure if that is % or what. I will get back to this next week! thanks for the replies They are all helpful.

Does anyone know the possible affects of higher Manganese (Mn) levels in 1008-1010 CRS? I received a lot with almost double the level as a previous lot and I'm wondering if this would make the material more porous when pretreating/cleaning for Ni plating. Any help would be greatly appriciated.

thanks for your help!

Does anyone know of any sites where I can access free MSDS's? I'm just looking for the MSDS on 99.99% Indium Thanks in advance, Aubry

thanks for your comments. I beleive that there is a CU flash, but I need to have my QC check the samples out before we know for sure- thanks again. This is a very helpful forum as always.-AT