To anyone who knows about this stuff...
Is there anywhere a list showing corrosive properties between metals. I need to know if the metals I am working with will be corrosive if I place them together. I work with a variety of carbon steels, stainless steels, coppers, etc. It would be invaluable to me to simply have a list in front of me to reference to see if the combonation I am proposing is feesible.
Thank you very much,
Zygfeld
Is there anywhere a list showing corrosive properties between metals. I need to know if the metals I am working with will be corrosive if I place them together. I work with a variety of carbon steels, stainless steels, coppers, etc. It would be invaluable to me to simply have a list in front of me to reference to see if the combonation I am proposing is feesible.
Thank you very much,
Zygfeld





RE: BIMETALLIC CORROSION PROBLEM
start.
Vince Maffei
RE: BIMETALLIC CORROSION PROBLEM
http://www.pemnet.com/design_information/galvanic.html
The chart from Mil Std 889
http://www.eaa1000.av.org/technicl/corrosion/galvanic.htm
Another location to get more info
http://www.nace.org/
Have a good day,
Rich
RE: BIMETALLIC CORROSION PROBLEM
www.corrosionsource.com/handbook/galv_series.htm