INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Glass fragments

Glass fragments

Glass fragments

(OP)
I am looking for the approximate size of glass fragments from a light bulb which exploded.  This light bulb was over a pool and the fragments are not easily retrievable.  However, I am concerned about them going through our strainers in the pool.  The strainer removes particles of 5mm or larger in size.  

I realize that any size is feasible, but what size is realistic?  

Any references would be great as well.  (I am nuclear and don't get into these kind of questions very much :)

Thanks in advance,

Cindy Ledbetter
cmledbetter@tva.gov

RE: Glass fragments

I can't help but think that the size particles depends on the size (and, hence, thickness of the glass ) and the manufacturer.

Might this be a question best answered by a little experiment on your part?

RE: Glass fragments

The size of the fragments will be proportional to the stress that broke it.  I have friends in the lighting industry to do further work if necessary, but I think you'll find them to be mostly large chunks with the exception of the point of origin.  There is a book out that discusses glass bottle breakage which will be the closest you'll find on the subject.  "Fractography of Glass" by Bradt and tressler.

RE: Glass fragments

I would suggest a little experiment.  Get one of the water filters used by back-packers (the "Katadhyn" sp? is best) which are used to filter out giardia and lung-worm cysts and see what if anything it picks up.

Because of "static fatigue" in a water envirnoment, the glass fragments will likely get smaller over time.

RE: Glass fragments

Disagree with the static fatigue theory.  No energy for fracture although plenty of fracture sites.  However a water environment will cause the glass to stain from calcium carbonate in the water....  I agree with glassman although you may need a basic fracture mechanics book to go along with Bradt and Tressler's compilation of articles...

RE: Glass fragments

Use toughened glass protective covers over bulbs. They almost never break.

-sajuvn@yahoo.com , India

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources