410 Creep properties
410 Creep properties
(OP)
Customer has informed that the material CA15 / A479 Ty410 Cond.2 has creep properties inferior to A182 GrF22 Cl.3 and above 400°C it is not advisable to use it. Could anybody clarify.
INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS Come Join Us!Are you an
Engineering professional? Join Eng-Tips Forums!
*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail. Posting GuidelinesJobs |
|
RE: 410 Creep properties
The are higher carbon cast stainless grades (martensitic, not ferritic) that would have better creep properties if you are looking for castings.
= = = = = = = = = = = = = = = = = = = =
P.E. Metallurgy, Plymouth Tube