I know that XLPE gets improved creep resistance as compared to just PE. I also understand hat nylons are generally creep resistant due to the crystallinity. I am wondering which would have higher creep resistance at higher temperature (110C); cross-linked polyethylene or nylon 11? The application would be rotomolded.
Red Flag Submitted
Thank you for helping keep Eng-Tips Forums free from inappropriate posts. The Eng-Tips staff will check this out and take appropriate action.
Reply To This Thread
Posting in the Eng-Tips forums is a member-only feature.
Cities are ceaseless engines of engineering activity. Itâ€™s likely that while you were on your way to work, you encountered a number of infrastructure development projects under construction. Download Now
When was the last time you drove down the highway without seeing a commercial truck hauling goods?The ubiquity of these machines underscores the important roll they play in modern commerce. Download Now