Hello!!
Is there a possibility of inappropriate Dew point causing Hydrogen Embrittlement while
hardening steel parts.?
Is there a possibility of inappropriate Dew point causing Hydrogen Embrittlement while
hardening steel parts.?





RE: Hydrogen embrittlement in heat treatment
RE: Hydrogen embrittlement in heat treatment
Material is SAE 52100,
Parameters 870 -20 min.
Martempering at 250-45 min.