INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Normalising

Normalising

Normalising

(OP)
I want to disscuse very simple issues but it is happend 2-3 parts in our heat treatment process.
part name Socket 304 wt per pc 0.520kg,material used EN8D C%-0.42, Mn%-0.85 and Raw material hardness is 179-187 BHN
loading per tray is 180 pcs
normalising temperature is set 860 degree and time 1hr 20min soaking ,7 tray furnace
part hardness required 162-210 BHN and hardness observed 156-170 BHN only proper fan cooling
than increase temperature 10 degree than little bit hardness achived 163 BHN
so plz suggest to me what can i do to improved hardness.

RE: Normalising

(OP)
will u tell be if Skt 220 we will increase tempreature 880°C against 860°C and time 25min against 20 mins /tray soaking than pc will burn.
and pc wt is 0.320kg loading 300 pc per tray.becoz specification is 175-220 BHN .material used EN8D C% 0.42,Mn%-0.86,Si%-0.25

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources