INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Carbon Steel Bold fracture

Carbon Steel Bold fracture

Carbon Steel Bold fracture

(OP)
Dear all,

I got this bolt that fractured during service. The screw does see some low cyclic tensile loads in the orders of ~10- 100 /day. Environment unknown. From the degradation of the zinc coating I would think some moisture but nothing severe.

It is Carbon steel 1025 Galvanized.
Take a look at the attached pics and let me know what you think.


RE: Carbon Steel Bold fracture

Are you sure it is 1025 steel? What is the hardness or strength level? The fracture looks like it initiated from the thread root at multiple locations. What you called striations may be crack arrest marks from step growth of the cracks. It looks like hydrogen embrittlement may be a possibility. Hard to say much more without more information on materials and environment.

RE: Carbon Steel Bold fracture

You should gently clean one of the fracture surfaces so you can better see fracture morphology better. The side with rust could be the origin side where there are ratchet marks indicating multiple origins (rust indicates that surface had existed longest). Look at the morphology under a stereobinocular microscope (try both the ring light and fiberoptic lighting) and look for evidence of whether fatigue had occurred. You will get good guidance on on the meaning of observed fatigue characteristics if you look at the schematic diagram in ASM Handbook Volume 11 Page 632 (I have also seen this same chart reproduced elsewhere).

Regarding material: you should look at the bolt head markings, which will tell you what material and associated properties you should expect.

Aaron Tanzer
www.lehightesting.com

RE: Carbon Steel Bold fracture

Not enough background information and no way to tell from the macrophotographs. Stop guessing and have it sent to a competent met lab.

PS; striations caused by fatigue crack propagation require much higher magnification to view. Crack arrest lines could be visible at this magnification.

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.