Smart questions
Smart answers
Smart people
INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Member Login
Remember Me
Forgot Password?
Join Us!

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips now!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
Join Eng-Tips
*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

LINK TO THIS FORUM!

Add Stickiness To Your Site By Linking To This Professionally Managed Technical Forum.
Just copy and paste the
code below into your site.

Eng-Tips LinkedIn® Group

Partner With Us!

"Best Of Breed" Forums Add Stickiness To Your Site
Partner Button
(Download This Button Today!)

Feedback

"...Many thanks to you for putting it together and to the forum members for taking the time to post their replies and give their time to help others. Their isn't another site that can touch it..."
More...

Geography

Where in the world do Eng-Tips members come from?
Click Here To Find Out!

Eng-Tips Shirts!

Get Eng-Tips Swag
Get your
Eng-Tips Forums
SWAG here!
Home > Forums > Materials Engineers > Activities > Material engineering other topics Forum

ASTM standard test method for ceramic flexural strength

thread367-322389
Read More Threads Like This One
limct (Mechanical)
21 May 12 6:51
hi all,

I am looking for the testing method for flexural strength of ceramic and I come across several different type. Does anyone know the difference between ASTM-F417, ASTM-F394 and ASTM-C1161?

Another question is, whether the speed of the loading will influence the flexural strength of the ceramic? Let's say we have 0.2mm/min and 0.5mm/min, how big would the difference between the two set of flexural strength be?

thanks.

Best regards,
ct

TVP (Materials)
22 May 12 12:33
F394 and F417 has been withdrawn and not replaced. You should use C1161 for your application. I don't have direct knowledge of the difference between 0.2 and 0.5 mm/s. This should be something that a provider of ceramic material could easily answer.
Read More Threads Like This One

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!

Back To Forum

Back To Material engineering other topics

Close Box

Join Eng-Tips® Today!

Join your peers on the Internet's largest technical engineering professional community.
It's easy to join and it's free.

Here's Why Members Love Eng-Tips Forums:

Register now while it's still free!

Already a member? Close this window and log in.

Join Us             Close