×
INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Tibor 3:1 is proved better that 5:1.Is there any thing better than3:1

Tibor 3:1 is proved better that 5:1.Is there any thing better than3:1

Tibor 3:1 is proved better that 5:1.Is there any thing better than3:1

(OP)
We have uesd 3:1 Tibor and it proved to be better that 5:1 in the grain sturcture and cost saving . Is some thing recommended other that 3:1 or how much boron should be there if we are casting alumium 6xxx series

RE: Tibor 3:1 is proved better that 5:1.Is there any thing better than3:1

I'm familiar with Tibor fishing reels and I assume that Tibor you a describing is an Aluminum Anodizing Process like the one used on the reels.
I don't have a clue as to the meaning of the ratios you provide.  

Can you post a link to their website?

RE: Tibor 3:1 is proved better that 5:1.Is there any thing better than3:1

(OP)
Thanks metengr this is what i was looking for  

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources