INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

softening properties of zinc

softening properties of zinc

softening properties of zinc

(OP)
I am looking for a way to soften zinc to make it as close to the softness of lead as possible.  This is not for structural use, it is for simulating lead without the hazards.

any ideas?

thanks
chris

RE: softening properties of zinc

(OP)
I looked into that, but need to keep costs relative to zinc/lead ($1.50/lb). That's why i was hoping to use zinc as a base metal.  I'm needing a few hundred pounds.

thanks

RE: softening properties of zinc

You can expect better answers if you elaborate on what the nature of the project is, i.e. what attributes of the test material are important.

RE: softening properties of zinc

(OP)
The project is to find a cost effective replacement for lead in the use of making test tool marks for forensic applications.  Currently, lead is used which has related health hazards.  Removing lead from the equation is the goal.

thanks

RE: softening properties of zinc

I hope to be proven wrong, but I think you're barking up the wrong tree here, trying to make one metal have the desirable properties of another without adding cost.

You could try bismuth or tin or alloys of either as lead substitutes if softness/malleability is what you're after,  but you're not getting away without this costing you substantially more than zinc will- or lead for that matter.

Any of these materials will be very easy to recycle if "test tool marks" are made in specimens that are then disposed of.

 

RE: softening properties of zinc

Does it need to be metallic? Surely you can find a wax with appropriate hardness.

RE: softening properties of zinc

do the opposite of killing a metal?

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources