INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

AISI 6150 Heat Treat

AISI 6150 Heat Treat

AISI 6150 Heat Treat

(OP)
It would be nice if some one could share after though harden heat treat data of actual parts contraction or expansion.

We are making a hollow gear shafts about 6" long
Unfortunately, I cannot post a print because of customer proprietary issues. Through Harden Heat Treat to 44HRc.
AISI 6150 Steel

I am looking for actual inch per inch expansion or contraction.
Any issues with distortion.

Thanks  
 

RE: AISI 6150 Heat Treat

What is the quenchant? Are you able to provide wall thickness?

RE: AISI 6150 Heat Treat

(OP)
.133 In. Thick wall

RE: AISI 6150 Heat Treat

(OP)
salt or oil (mar temper or mar quench)

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources