pipeline for transportation of supercritical co2
pipeline for transportation of supercritical co2
(OP)
Hi Guys, I'm new to this forum.
I hope I have posted this in the correct forum.
I have been asked if the API 5L grade B Plus material would be a suitable material to reduce the likelihood of fracture propagation.
I have a hunch as how to approach this problem, but seeing as I am unsure, I was wondering how others might tackle this problem.
Thanks in anticipation,
Frank
I hope I have posted this in the correct forum.
I have been asked if the API 5L grade B Plus material would be a suitable material to reduce the likelihood of fracture propagation.
I have a hunch as how to approach this problem, but seeing as I am unsure, I was wondering how others might tackle this problem.
Thanks in anticipation,
Frank





RE: pipeline for transportation of supercritical co2
RE: pipeline for transportation of supercritical co2
Crack propagating resistance if not stiffener rings, if not both is a favorable quality.
There's pleanty of internet info available. Just search for "crack propagation CO2 pipelines"
http://virtualpipeline.spaces.msn.com
"What gets us into trouble is not what we don't know, its what we know for sure" - Mark Twain