INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Thick Section Rubber Molding

Thick Section Rubber Molding

Thick Section Rubber Molding

(OP)
Greetings Rubber head Guru's

We are accomplished molders but have never ventured into the thick section molding. I currently have a contract to mold a 6"diameter by 8.5" cylinder (top and bottom edges have a 2" radius fillet). I'm searching for info on cure times, more or less shrinkage due to the thick section, how to overcome Backrind or other molding defects.

Thanks and God Bless
Sluggo

RE: Thick Section Rubber Molding

Sluggo,
A couple of questions:
What type of compound are you molding, polymer-wise and cure system-wise (sulfur or peroxide?), and what are the compound's curing characteristics? Do you have curemeter data? Does the compound revert upon over-curing (like natural rubber)?

I'm not a molding expert, but I'm pretty sure that the answers to these questions will help others give you some guidance.

Tom Jablonowski, TSE Industries, Inc.
www.tse-industries.com

RE: Thick Section Rubber Molding

Large thick sections often require lower temperature and slower cures. Lower temperature give you a longer time before reversion occurs. You need really good packing, but the rubber can't be moving out the overflows once it has started to crosslink. Make sure you are getting enough cure in the middle. Cut when cool to look for bubbles or use an embedded thermocouple to monitor actual temperatures. Shrinkage can be different, but I've never found a better way than to just measure it and cut steel.

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources