INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

Vibratory Stress relief

Vibratory Stress relief

Vibratory Stress relief

(OP)
We are currently having molds built in China and they are using Vibratory Stress relief on the Core and Cavity blocks.  These blocks are made out of p20, will we have any issues with the blocks after this method has been complete?

RE: Vibratory Stress relief

not very likely.

I used to work on the floor of a shop that built molds for huge facias on cars and truks (you would have a 25-30 ton cavity or core)

Never had a problem.


The machine usually prints out a graph...so make sure the graph is upto the specks (what the manufacturer of the machine recomends)


The only trick is,  It has to be done right.

lot of times we would run it on each end of the mold, where the most material has been removed, (3 times on each end is recomended)

RE: Vibratory Stress relief

You can treat it just one time, if you use the right equipment and procedure.  See:

 http://vsrtechnology.net

BK

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources