INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

303S vs 304L

303S vs 304L

303S vs 304L

(OP)
How does 304L compare to 303S on the basis of corrosion resistance and machinability?  Also experimenting with 316L; but cost concerns and machinability point to 304L.  Any help in this manner would be very much appreciated.  (303S is what we currently use, but would like to use a metal that does not need to be plated in order to reach desired corrosion resistance).     

RE: 303S vs 304L

use the 304 maxival. it is much more easier to machine/

RE: 303S vs 304L

The 303S is considered a "free machining" stainless. It has a machinability factor that is better than 304L or 316L. However, you will sacrifice corrosion resistance with this material. I recommend going with the 316L. You can spend a little extra on the material and buy from Carpenter. Their material is manufactured using a more refined process than some other commodity steel manufacturers. What you lose in the extra material cost will easily be made back up with less tool wear and downtime.

Good luck!

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources