INTELLIGENT WORK FORUMS
FOR ENGINEERING PROFESSIONALS

Log In

Come Join Us!

Are you an
Engineering professional?
Join Eng-Tips Forums!
  • Talk With Other Members
  • Be Notified Of Responses
    To Your Posts
  • Keyword Search
  • One-Click Access To Your
    Favorite Forums
  • Automated Signatures
    On Your Posts
  • Best Of All, It's Free!
  • Students Click Here

*Eng-Tips's functionality depends on members receiving e-mail. By joining you are opting in to receive e-mail.

Posting Guidelines

Promoting, selling, recruiting, coursework and thesis posting is forbidden.

Students Click Here

Jobs

LOW TEMPERATURE SERVICE WELDING PROCEDURES

LOW TEMPERATURE SERVICE WELDING PROCEDURES

LOW TEMPERATURE SERVICE WELDING PROCEDURES

(OP)
CAN ANYONE PROVIDE A WELDING PROCEDURE WITH NO PRE-HEAT TREATMENT FOR WELDING PIPE FOR COLD (LOW) TEMPERATURE SERVICE?
THE PIPE MATERIAL WILL BE API 5L X52 OR DUPLEX SS.

RE: LOW TEMPERATURE SERVICE WELDING PROCEDURES

Duplex does not require preheat in any case, air dryers needed only to expel mositure. API 5L x52 with no preheat is regular welding. What are the thicknesses involved, the process/consumables planned, the grade of the duplex, the temperature for the LOW TEMPERATURE SERVICE. Please provide more details.

Thanks and regards
Sayee Prasad R
Ph: 0097143968906
Mob: 00971507682668
email: sayee_prasad@yahoo.com
If it moves, train it...if it doesn't move, calibrate it...if it isn't written down, it never happened!

Red Flag This Post

Please let us know here why this post is inappropriate. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Red Flag Submitted

Thank you for helping keep Eng-Tips Forums free from inappropriate posts.
The Eng-Tips staff will check this out and take appropriate action.

Reply To This Thread

Posting in the Eng-Tips forums is a member-only feature.

Click Here to join Eng-Tips and talk with other members!


Resources